Aermet100钢制坯工艺对微观组织和力学性能的影响

针对Aermet100钢研究了大规格棒材锻造工艺对微观组织和力学性能的影响.研究结果表明:细化锻造过程的晶粒度有利于获得较高的断裂韧度.细化晶粒度的途径主要有锻造加工温度控制在再结晶区间和增大总变形比.Aermet 100钢锻造温度区间应控制在950～1100℃之间进行,终锻温度控制在950～1000℃;总变形比之和应大于20.     

Z1Cr18Ni9Ti不锈钢法兰的铸造工艺研究

本文介绍了一种Z1Cr18Ni9Ti零件的制造方法，即用铸造方法。这种方法可以节省材料，提高效率，降低成本，并在此基础上探讨了有效的熔炼和铸造工艺。     

45CrNiMo1V超高强度钢研制及应用

介绍了４５ＣｒＮｉＭｏ１Ｖ超高强度钢的相变温度、冷却转变曲线、热处理工艺参数，物理性能、冷成形和焊接工艺性能及应用状况。为应用该钢提供了有用的试验数据。     

钢与胶粘剂粘接界面的XPS分析

结合氩离子枪刻蚀技术，用X射线电子能谱(XPS)对钢与胶粘剂粘接的界面进行研究，分析了粘接过程中元素的化学环境变化，并对粘接机理进行了探讨。结果表明，胶粘剂中酚醛树脂在界面区域与钢之间存在化学结合，而氯化橡胶与钢之间以范德华力粘接。     

固体发动机壳体用D406A钢锻件的断裂韧度KIC测试研究

对固体发动机壳体用D406A超高强度锅锻件,进行了平面应变断裂韧度K_(IC)测试研究,获得了壳体重要部位实用锻件的K_(IC)值;找到了材料强度和断裂韧度合理匹配的碳含量范围,为壳体设计与安全使用及断裂分析提供了试验依据。     

304不锈钢的应力腐蚀断裂

用慢应变速率技术研究了敏化的304不锈钢在氧饱和的NaCl溶液中的应力腐蚀断裂(SCC)行为以及浓度、温度和电位的影响。结果表明,在90℃1000ppmNaCl溶液中,在5.5×10~(-6)s~(-1)应变速率下,电位大于-0.5V(相对于SCE,下同)有应力腐蚀敏感性。随着应变速率提高、浓度减小或温度降低,断裂电位范围移向较正的电位(-0.2V以上)。在较慢的应变速率下,在-0.5～-0.2V产生单裂纹;高于-0.2V对于所用的两种应变速率都产生多裂纹;低于-0.6V未发现裂纹。该体系的自腐蚀电位在-0.25V附近,处于SCC敏感区。恒电位下动态应变试验中电流增量与平均裂纹速度在双对数座标上呈正比关系,表明该体系的沿晶SCC本质上受溶解控制。     

泡沫钢的制备及三点弯曲性能

为了制备孔隙率较高、孔结构均匀、性能优良的泡沫钢板及夹芯复合板,以316L不锈钢粉为原料,Ca Cl2为造孔剂,采用粉末冶金烧结-溶解法制备不同孔隙率、孔径的泡沫钢,并用物理粘接法制备泡沫钢夹芯复合板。通过对泡沫钢板和夹芯复合板进行三点弯曲实验研究两者的抗弯曲性能。观察泡沫钢板的三点弯曲变形过程,分析孔隙率和孔径对泡沫钢板和夹芯复合板抗弯曲性能的影响,对比两者的极限抗弯载荷变化。结果表明:泡沫钢板的变形首先从薄壁不规则的孔壁开始,形成裂纹并进行扩展,最终导致宏观断裂;对于泡沫钢夹芯复合板,当孔隙率从69.4%增加至82.5%时,其所能承受的极限载荷从2345 N下降至1254 N,在相同孔隙率下,相比于泡沫钢板,夹芯板承受的极限弯曲载荷提升了15%~43%;当孔径从1.9 mm增加至3.9 mm,孔隙率约为73%时,其所能承受的极限弯曲载荷从2070 N下降至1528 N,与泡沫钢板相比,相同孔径下,夹芯板承受的极限弯曲载荷提升了15%~28%;在孔隙率和孔径相同条件下,泡沫钢夹芯复合板的抗弯承载能力比泡沫钢板提高15%以上。     

Analysis of the current density characteristics in through-mask electrochemical micromachining (TMEMM) for fabrication of micro-hole arrays on invar alloy film

Invar alloy consisting of 64% iron and 36% nickel has been widely used for the production of shadow masks for organic light emitting diodes(OLEDs) because of its low thermal expansion coefficient(1.86 ? 10à6cm/°C).To fabricate micro-hole arrays on 30 lm invar alloy film,through-mask electrochemical micromachining(TMEMM) was developed and combined with a portion of the photolithography etching process.For precise hole shapes,patterned photoresist(PR) film was applied as an insulating mask.To investigate the relationship between the current density and the material removal rate,the principle of the electrochemical machining was studied with a focus on the equation.The finite element method(FEM) was used to verify the influence of each parameter on the current density on the invar alloy film surface.The parameters considered were the thickness of the PR mask,inter-electrode gap(IEG),and electrolyte concentration.Design of experiments(DOE) was used to figure out the contribution of each parameter.A simulation was conducted with varying parameters to figure out their relationships with the current density.Optimization was conducted to select the suitable conditions.An experiment was carried out to verify the simulation results.It was possible to fabricate micro-hole arrays on invar alloy film using TMEMM,which is a promising method that can be applied to fabrications of OLEDs shadow masks.     

Relationship Between Corrosion Level of Steel Bar and Diameter of Corroded Sensing Steel Wire in Wireless Sensor

A kind of wireless sensor was previously developed,which is powered and transmit signals wirelessly instead of using an electrical connection to the embedded reinforcement.Based on this technique,the relationship between diameters of corroded sensing steel wires and corrosion levels of steel bars is established by experiments.Quadratic function is utilized to fit the experiment results,and the correlation coefficients are all larger than 0.95.Estimated corrosion levels of commonly used steel bars are given for different diameters of corroded sensing steel wires fractured due to corrosion.     

SA-335P122材料管道焊接工艺研究

通过对1000MW超超临界锅炉四级过热器出口集箱和主蒸汽管道进行试验研究,发现锅炉管道存在环缝焊接式样不合格的问题.通过对管道SA-335P122材料进行力学性能分析,并结合试验数据,提出了新的工艺流程,采用了新的焊接材料和焊接工艺,通过试验验证了焊接流程的合理性,使产品制造一次合格.